304L 10 * 1mm asye pur tib mawonnen soti nan manifakti Lachin
Konpozisyon chimik ak pwopriyete fizik nan asye pur
304L 10 * 1mm asye pur tib mawonnen soti nan manifakti Lachin
| Materyèl | ASTM A269 Chimik Konpozisyon % Max | ||||||||||
| C | Mn | P | S | Si | Cr | Ni | Mo | NB | Nb | Ti | |
| TP304 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 18.0-20.0 | 8.0-11.0 | ^ | ^ | ^ . | ^ |
| TP304L | 0.035 | 2.00 | 0.045 | 0.030 | 1.00 | 18.0-20.0 | 8.0-12.0 | ^ | ^ | ^ | ^ |
| TP316 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 16.0-18.0 | 10.0-14.0 | 2.00-3.00 | ^ | ^ | ^ |
| TP316L | 0.035 D | 2.00 | 0.045 | 0.030 | 1.00 | 16.0-18.0 | 10.0-15.0 | 2.00-3.00 | ^ | ^ | ^ |
| TP321 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 | ^ | ^ | ^ | 5C -0.70 |
| TP347 | 0.08 | 2.00 | 0.045 | 0.030 | 1.00 | 17.0-19.0 | 9.0-12.0 | 10C -1.10 | ^ | ||
| Materyèl | Tretman chalè | Tanperati F (C) Min. | Dite | |
| Brinell | Rockwell | |||
| TP304 | Solisyon | 1900 (1040) | 192HBW/200HV | 90HRB |
| TP304L | Solisyon | 1900 (1040) | 192HBW/200HV | 90HRB |
| TP316 | Solisyon | 1900 (1040) | 192HBW/200HV | 90HRB |
| TP316L | Solisyon | 1900 (1040) | 192HBW/200HV | 90HRB |
| TP321 | Solisyon | 1900(1040) F | 192HBW/200HV | 90HRB |
| TP347 | Solisyon | 1900 (1040) | 192HBW/200HV | 90HRB |
| OD, pous | OD tolerans pous (mm) | WT Tolerans % | Longè Tolerans pous (mm) | |
| + | - | |||
| ≤ 1/2 | ± 0.005 (0.13) | ± 15 | 1/8 (3.2) | 0 |
| > 1 / 2 ~ 1 1 / 2 | ± 0.005 (0.13) | ± 10 | 1/8 (3.2) | 0 |
| > 1 1 / 2 ~ < 3 1 / 2 | ± 0.010 (0.25) | ± 10 | 3/16 (4.8) | 0 |
| > 3 1 / 2 ~ < 5 1 / 2 | ± 0.015 (0.38) | ± 10 | 3/16 (4.8) | 0 |
| > 5 1 / 2 ~ < 8 | ± 0.030 (0.76) | ± 10 | 3/16 (4.8) | 0 |
| 8~<12 | ± 0.040 (1.01) | ± 10 | 3/16 (4.8) | 0 |
| 12~< 14 | ± 0.050 (1.26) | ± 10 | 3/16 (4.8) | 0 |