304 ak 316 SS Capillary Coil Tubes founisè nan Lachin
304 ak 316 SS Capillary Coil Tubes founisè nan Lachin
Gen diferan klas materyèl ke yo itilize pou tib an bobin pou echanjeur chalè, chodyèr, aparèy chofaj super ak lòt aplikasyon pou tanperati ki wo ki enplike chofaj oswa refwadisman.Diferan kalite yo genyen ladan yo 3/8 mawonnen en fe tubing tou.Tou depan de nati aplikasyon an, nati likid ki transmèt nan tib yo ak klas materyèl yo, kalite tib sa yo diferan.Gen de dimansyon diferan pou tib yo bobin kòm dyamèt tib la ak dyamèt bobin la, longè, epesè miray ak orè yo.Tib bobin SS yo itilize nan diferan dimansyon ak klas selon kondisyon aplikasyon yo.Gen materyèl alyaj segondè ak lòt materyèl asye kabòn ki disponib pou tib la bobin tou.
Konpatibilite chimik nan tib bobin asye pur
| Klas | C | Mn | Si | P | S | Cr | Mo | Ni | N | Ti | Fe | |
| 304 | min. | 18.0 | 8.0 | |||||||||
| max. | 0.08 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | 0.10 | ||||
| 304L | min. | 18.0 | 8.0 | |||||||||
| max. | 0.030 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 12.0 | 0.10 | ||||
| 304H | min. | 0.04 | 18.0 | 8.0 | ||||||||
| max. | 0.010 | 2.0 | 0.75 | 0.045 | 0.030 | 20.0 | 10.5 | |||||
| SS 310 | 0.015 max | 2 max | 0.015 max | 0.020 max | 0.015 max | 24.00 26.00 | 0.10 max | 19.00 21.00 | 54.7 min | |||
| SS 310S | 0.08 max | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 0.75 max | 19.00 21.00 | 53.095 min | |||
| SS 310H | 0.04 0.10 | 2 max | 1.00 max | 0.045 max | 0.030 max | 24.00 26.00 | 19.00 21.00 | 53.885 min | ||||
| 316 | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316L | min. | 16.0 | 2.03.0 | 10.0 | ||||||||
| max. | 0.035 | 2.0 | 0.75 | 0.045 | 0.030 | 18.0 | 14.0 | |||||
| 316TI | 0.08 max | 10.00 14.00 | 2.0 max | 0.045 max | 0.030 max | 16.00 18.00 | 0.75 max | 2.00 3.00 | ||||
| 317 | 0.08 max | 2 max | 1 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 57.845 min | ||||
| SS 317L | 0.035 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 18.00 20.00 | 3.00 4.00 | 11.00 15.00 | 57.89 min | |||
| SS 321 | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 5 (C + N) 0.70 max | |||
| SS 321H | 0.04 0.10 | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 19.00 | 9.00 12.00 | 0.10 max | 4 (C + N) 0.70 max | |||
| 347/ 347H | 0.08 max | 2.0 max | 1.0 max | 0.045 max | 0.030 max | 17.00 20.00 | 9.0013.00 | |||||
| 410 | min. | 11.5 | ||||||||||
| max. | 0.15 | 1.0 | 1.00 | 0.040 | 0.030 | 13.5 | 0.75 | |||||
| 446 | min. | 23.0 | 0.10 | |||||||||
| max. | 0.2 | 1.5 | 0.75 | 0.040 | 0.030 | 30.0 | 0.50 | 0.25 | ||||
| 904L | min. | 19.0 | 4.00 | 23.00 | 0.10 | |||||||
| max. | 0.20 | 2.00 | 1.00 | 0.045 | 0.035 | 23.0 | 5.00 | 28.00 | 0.25 | |||
Pwopriyete mekanik Tablo nan bobin tib asye pur
| Klas | Dansite | Pwen k ap fonn | Fòs rupture | Fòs Sede (0.2% Offset) | Elongasyon |
| 304/ 304L | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 304H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 40% |
| 310 / 310S / 310H | 7.9 g/cm3 | 1402 °C (2555 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 40% |
| 306/ 316H | 8.0 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 316L | 8.0 g/cm3 | 1399 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 317 | 7.9 g/cm3 | 1400 °C (2550 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 321 | 8.0 g/cm3 | 1457 °C (2650 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 347 | 8.0 g/cm3 | 1454 °C (2650 °F) | Psi 75000, MPa 515 | Psi 30000, MPa 205 | 35% |
| 904L | 7.95 g/cm3 | 1350 °C (2460 °F) | Psi 71000, MPa 490 | Psi 32000, MPa 220 | 35% |
SS Chalè Echanjeur Mawonnen Tib Klas ekivalan
| STANDARD | WERKSTOFF NR. | UNS | JIS | BS | GOST | AFNOR | EN |
| SS 304 | 1.4301 | S30400 | SUS 304 | 304S31 | 08Х18Н10 | Z7CN18-09 | X5CrNi18-10 |
| SS 304L | 1.4306 / 1.4307 | S30403 | SUS 304L | 3304S11 | 03Х18Н11 | Z3CN18‐10 | X2CrNi18-9 / X2CrNi19-11 |
| SS 304H | 1.4301 | S30409 | – | – | – | – | – |
| SS 310 | 1.4841 | S31000 | SUS 310 | 310S24 | 20Ch25N20S2 | – | X15CrNi25-20 |
| SS 310S | 1.4845 | S31008 | SUS 310S | 310S16 | 20Ch23N18 | – | X8CrNi25-21 |
| SS 310H | – | S31009 | – | – | – | – | – |
| SS 316 | 1.4401 / 1.4436 | S31600 | SUS 316 | 316S31 / 316S33 | – | Z7CND17-11-02 | X5CrNiMo17-12-2 / X3CrNiMo17-13-3 |
| SS 316L | 1.4404 / 1.4435 | S31603 | SUS 316L | 316S11 / 316S13 | 03Ch17N14M3 / 03Ch17N14M2 | Z3CND17-11-02 / Z3CND18-14-03 | X2CrNiMo17-12-2 / X2CrNiMo18-14-3 |
| SS 316H | 1.4401 | S31609 | – | – | – | – | – |
| SS 316Ti | 1.4571 | S31635 | SUS 316Ti | 320S31 | 08Ch17N13M2T | Z6CNDT17‐123 | X6CrNiMoTi17-12-2 |
| SS 317 | 1.4449 | S31700 | SUS 317 | – | – | – | – |
| SS 317L | 1.4438 | S31703 | SUS 317L | – | – | – | X2CrNiMo18-15-4 |
| SS 321 | 1.4541 | S32100 | SUS 321 | – | – | – | X6CrNiTi18-10 |
| SS 321H | 1.4878 | S32109 | SUS 321H | – | – | – | X12CrNiTi18-9 |
| SS 347 | 1.4550 | S34700 | SUS 347 | – | 08Ch18N12B | – | X6CrNiNb18-10 |
| SS 347H | 1.4961 | S34709 | SUS 347H | – | – | – | X6CrNiNb18-12 |
| SS 904L | 1.4539 | N08904 | SUS 904L | 904S13 | STS 317J5L | Z2 NCDU 25-20 | X1NiCrMoCu25-20-5 |